|Curing Temperature||> 190 C|
|Resistivity||2 - 10 x of bulk gold|
|Printable Material||Polyimide, ITO, Glass,many others|
|Particles size||~ 10 nm|
|Nanosilver concentration||25 - 60 wt%|
Viscosity (can be controlled for specific application)
|1 - 30 cP|
|Shelf life||> 3 months at room temperature|
TEM of silver nanopaticles
UTDAu Conductive Gold Nanoinks
UTDAu gold nanoink is general-use ink for aerosol or ink-jet printing on variety of substrates. UTDAu is based on gold nanoparticles with average size around 4 nm and dispersed in a liquid vehicle. Since they are surface stabilized, UTDAu inks are highly soluble in nonpolar organic solvents and stable under atmospheric conditions at room temperature.
TEM of gold nanopaticles
|Curing Temperature||120 - 130 C|
|Resistivity, curing at 130 C, 120 min||~ 10 micro Ohms - cm|
|Resistivity, curing at 200 C, 10 min||~ 3 micro Ohms - cm|
|Printable material||PET, Polyimide, ITO, glass, Teslin, Silicon,many others|
|Particle Size||~ 3 - 5 nm|
|Nano gold concentration||~ 25 - 60 wt%|
|Viscosity (can be adjusted for specific application)||1 - 30 cP|
|Shelf Life||3 months at room temperature|
Silver nanoparticles have a low sintering temperature and can be used on inexpensive substrates, such as paper, polyester, polyimide and others.
The resistivity of UTDAg ink decreases with time at required temperatures.
LIST OF PRODUCTS
|UTDAg40X||Silver nanoink in xylenes||Aerosol-Jet (UA (1))||25 - 40 w/v% (3)||PET||~120-140 C|
|UTDAg40IJ ||Silver nanoink in solvent mixture|
Ink-Jet: Microfab, Dimatix, MicroDrop, SonoPlot,
|55 - 60 w/v% ||Kapton, Silicon, PC, Stainless steel||~130 C|
|UTDAg40TE||Silver nanoink in solvent mixture||Aerosol-Jet (UA), SonoPlot||25 - 40 w/v%||Kapton, Silicon, PC, Stainless steel||~120-140 C|
|UTDAgPA||Silver nanoink in solvent mixture||Aerosol-Jet (PA (2)), SonoPlot||~ 80 - 100 w/v%||Kapton, Silicon, PC, Stainless steel||~140 C|
|NSEP||Dielectric ink||Ink-Jet, Microfab, Dimatix, SonoPlot||10-15%||Kapton, glass, silicon, many others||~140 C|
1 UA – Ultrasonic Atomizer
2 PA – Pneumatic Atomizer
3 Inks can be prepared with different concentration upon request. Typical concentrations are given in the Table above.
Gold nanoinks are formulated in the same solvents or solvent mixtures as silver nanoinks. Minimum curing temperature for gold nanoinks: 190-200 C.
All inks can be printed on glass. To improve adhesion to glass and other polar surfaces we provide an additive - adhesion promoter.
Please contact us for prices, quantities, and solvent specifications.
Gold nanoparticles have a low sintering temperature and can be printed on ITO and glass substrates. The resistivity of UTDAu40 ink decreases with time at required temperatures.
Silver Lines and Dots printed by Ink-Jet
Gold Lines and Dots printed by Aerosol-Jet
For Printed Electronics
UTDAg Conductive Silver Nanoinks
UTDAg silver nanoink is general-use ink for aerosol or ink-jet printing on variety of substrates. UTDAg is based on silver nanoparticles with average size around 10 nm and dispersed in a liquid vehicle. Since they are surface stabilized, UTDAg inks are highly soluble in nonpolar organic solvents and stable under atmospheric conditions at room temperature.
Our nanoinks are formulated to work with the Aerosol Jet and Ink-Jet printers.
Please visit: www.optomec.com for more information on Aerosol-Jet printing.
For ink-jet printing please visit:
MicroFab Technologies: www.microfab.com
MicroDrop Technologies: www.microdrop.de
SonoPlot, Inc.: www.sonoplot.com